Transparent Epoxy Resin Hlakileng Kamore ea Mocheso Pheko le Viscosity e tlase
Thepa:
Viscosity e tlase
Ponaletso e babatsehang
Pheko ea mocheso oa kamore
Mokhoa o khothalelitsoeng:
Ho lahla
Lintlha tsa Motheo | |||
Resin | GE-7502A | Standard | |
Karolo | Mokelikeli o bonaletsang o se nang mebala | - | |
Viscosity ho 25℃ [mPa·s] | 1,400-1,800 | GB/T 22314-2008 | |
Boima ba 'mele [g/cm3] | 1.10-1.20 | GB/T 15223-2008 | |
Boleng ba Epoxide [eq/100 g] | 0.53-0.59 | GB/T 4612-2008 | |
Hardener | GE-7502B | Standard | |
Karolo | Seela se se nang mmala se bonaletsang | - | |
Viscosity ho 25℃ [mPa·s] | 8-15 | GB/T 22314-2008 | |
Boleng ba Amine [mg KOH/g] | 400-500 | WAMTIQ01-018 | |
Ts'ebetso ea Lintlha | |||
Kopanya Karolelano | Resin:Hardener | Karolelano ka boima ba 'mele | Karolelano ka molumo |
GE-7502A : GE-7502B | 3:1 | 100:37-38 | |
Viscosity ea Motsoako oa Pele | GE-7502A : GE-7502B | Standard | |
[mPa·s] | 25 ℃ | 230 | WAMTIQ01-003 |
Bophelo ba Pitsa | GE-7502A : GE-7502B | Standard | |
[mets] | 25 ℃ | 180-210 | WAMTIQ01-004 |
Phetoho ea khalasemochesoTg [℃] | GE-7502A : GE-7502B | Standard | |
60 °C × 3 h + 80 °C × 3 h | ≥60 | GB/T 19466.2-2004 |
Recommended Conditioning ea Pheko: | ||
Botenya | Pheko ea pele | Kalafo ea poso |
≤ 10 limilimithara | 25 °C × 24 h kapa 60 °C × 3 h | 80 °C × 2 h |
> 10 limilimithara | 25 °C × 24 h | 80 °C × 2 h |
Thepa ea ho Lahlela Resin | |||
Boemo ba ho folisa | 60 °C × 3 h + 80 °C × 3 h | Standard | |
Sehlahisoa mofuta | GE-7502A/GE-7502B | - | |
Flexural matla [MPa] | 115 | GB/T 2567-2008 | |
Flexural modulus [MPa] | 3456 | GB/T 2567-2008 | |
Matla a hatellang [MPa] | 87 | GB/T 2567-2008 | |
Compressive modulus [MPa] | 2120 | GB/T 2567-2008 | |
Hardness Shore D | 80 | ||
Sephutheloana | |||
Resin | IBC Ton barrel: 1100kg / ea; Drum ea tšepe: 200kg / ea;Buckle Bucket: 50kg / ea; | ||
Hardener | IBC Ton barrel: 900kg / ea; Drum ea tšepe: 200kg / ea;Bucket ea polasetiki: 20kg / ea; | ||
Hlokomela: | Sephutheloana se ikhethileng se teng |
Litaelo |
Ho hlahloba hore na ho na le crystallization ho moemeli oa GE-7502A pele u e sebelisa.Haeba ho na le crystallization, mehato e lokela ho nkoa ka tsela e latelang: Ha ea lokela ho sebelisoa ho fihlela crystallization e qhibiliha ka ho feletseng 'me mocheso oa ho baka ke 80 ℃. |
Polokelo |
1. GE-7502A mohlomong crystallize ka mocheso tlaase. |
2. Se ke oa pepesa tlas'a khanya ea letsatsi 'me u boloke sebakeng se hloekileng, se phodileng le se omileng. |
3. E tiisitsoe hang ka mor'a tšebeliso. |
4. E khothalletsoang bophelo ba sethala sa lihlahisoa - likhoeli tse 12. |
Ho Tšoara Litlhokomelo | |
Lisebelisoa tsa Tšireletso ea Motho | 1. Apara liatlana tsa tšireletso ho qoba ho kopana ka ho toba le letlalo. |
Tšireletso ea ho Phefumoloha | 2. Ha ho tšireletso e khethehileng. |
Tshireletso ya Mahlo | 3. Li-goggles tsa lik'hemik'hale tse thibelang ho hasana le sefahleho li khothalletsoa. |
Tšireletso ea 'Mele | 4. Sebelisa seaparo sa tšireletso se ka hanetsoang, lieta tsa tšireletso, liatlana, seaparo le lisebelisoa tsa metsi tsa tšohanyetso ho latela maemo. |
Thuso ea pele | |
Letlalo | Hlatsoa ka metsi a futhumetseng a sesepa bonyane metsotso e 5 kapa tšilafalo e tlosoe. |
Mahlo |
|
Ho hema |
|
Tsebiso ea bohlokoa:
Lintlha tse hlahang khatisong ena li ipapisitse le liteko tsa boemo bo itseng tsa Wells Advanced Materials (Shanghai) Co., Ltd. Ka lebaka la lintlha tse ngata tse ka amang ts'ebetso le ts'ebeliso ea lihlahisoa tsa rona, lintlha tsena HA U HLOKOMELA li-processor ho sebetsa. lipatlisiso le liteko tsa bona.Ha ho letho ka mona le lokelang ho nkoa e le waranti.Ke boikarabello ba mosebelisi ho tseba ho sebetsa ha tlhahisoleseling le likhothaletso le ho tšoaneleha ha sehlahisoa sefe kapa sefe bakeng sa merero ea sona e ikhethileng.